Adhesive epoxy Scotch-Weld DP420NS black biocomponent 3M

Adhesive epoxy Scotch-Weld DP420NS black color 3M. When using Duo-Pak (DP)-size adhesives, trust the Duo-Pak dispenser equipment 3M to achieve practical and accurate measurement, mixing and dispensing.

The epoxy adhesive 3MTM Scotch-WeldTM DP420NS is a black epoxy structural adhesive, reinforced, bicomponent and non-discovery, which provides good overall resistance as well as high impact resistance and fatigue to meet the most demanding union challenges. The epoxy adhesive 3MTM Scotch-Weld DP420NS can replace mechanical braces, screws, rivets and welding points in many applications. When using Duo-Pak (DP)-size adhesives, trust the Duo-Pak dispenser equipment 3M to achieve practical and accurate measurement, mixing and dispensing. Its high clutch and peel resistance maintains durable bonds at high and low temperatures Our epoxy adhesive 3MTM Scotch-WeldTM DP420NS maintains its bond resistance at high and low temperatures and can withstand powder paint operations up to 204 °C for 60 minutes. It works well on various substrates such as metals, ceramics, wood, glass, many composites and plastics, and is an excellent binding agent inside for applications of adhesion, gluing, filling, paneling and structural joints.

The epoxy adhesive 3MTM Scotch-WeldTM DP420NS meets the requirements of UL 94 HB. 20 minute mix life that allows positioning and adjustments The epoxy adhesive 3MTM Scotch-WeldTM DP420NS reaches the clamping of parts in about two hours and cures completely in 24 hours at 22 °C. The mixing ratio is 2:1 and offers a mixing life of 20 minutes, enough to make the necessary settings before it heals. This adhesive is available in presentations of different sizes and can be dispensed in various ways to meet the demands of various users and jobs. Reinforced, which makes it resistant to impacts and fatigue.

The epoxy adhesive 3MTM Scotch-WeldTM DP420NS is suitable for applications facing severe environmental conditions. Formulated to provide strong long-term adherence, this elastic adhesive epoxy is another of the ways in which 3M apply your experience to meet and exceed expectations of even the most demanding applications.

What are the epoxy adhesives? The epoxy adhesives are part of the family of the so-called "structural adhesives", including acrylic, polyurethane and cyanoacrylate. Epoxys are formulated as liquid reagent polymers that undergo a chemical reaction when mixed and then cure to form a solid plastic material. Once the two components are mixed in the specified relationship, start.

Supply: from 5 to 10 working days

CHARACTERISTICS

• Its high clutch and peel resistance maintains durable bonds at high and low temperatures.
• Reinforced, which makes it resistant to impacts and fatigue.
• 20 minute mix life that allows positioning and adjustments.
• Its formulation prevents it from recalling, which guarantees its permanence in the place of application

SPECIFICATIONS

UL94 HB

Design Challenges

Absorption of impacts and blows, Noise control, vibrations and NVH roughness

Sectors

Consumer Goods, Electronics, General Industry, MRO, Transport, Army and Government

Recipient size (metric system)

50 ml, 400 ml

Storage temperature

60-80 F (16-27 C)

Storage temperature (Celsius)

16°C - 27°C

Cured time

20 min @ 72 °F (22 °C)

Type of Adhesive

Epoxi

Product type

Epoxy adhesive

Units by Kit

12.0

Mixing life

15 min - 30 min

Life in months (from date of manufacture)

15 

Viscosity

Don't let him go

Volume

50 mL

BENEFITS

• Its high clutch and peel resistance maintains durable bonds at high and low temperatures.
• It works well on various substrates such as metals, ceramics, wood, glass, many composites and plastics, and is an excellent binding agent inside for applications of adhesion, gluing, filling, paneling and structural joints.
• Union with carbon fiber epoxy Mixing life of 20 minutes that allows positioning and adjustments.
• The epoxy adhesive 3MTM Scotch-WeldTM DP420 reaches the clamping of parts in about two hours and cures completely in 24 hours at 22 °C.
• Reinforced, which makes it resistant to impacts and fatigue.
• The epoxy adhesive 3MTM Scotch-WeldTM DP420 is suitable for applications facing severe environmental conditions.
• Formulated to provide strong long-term adherence, this elastic epoxy adhesive is another way in which 3M meets and exceeds the expectations of even the most demanding applications.
• What are the epoxy adhesives? The epoxy adhesives are part of the family of the so-called "structural adhesives", including acrylic, polyurethane and cyanoacrylate. Epoxys are formulated as liquid reagent polymers that undergo a chemical reaction when mixed and then cure to form a solid plastic material.

APPLICATIONS

The epoxy adhesive 3MTM Scotch-WeldTM DP420NS is a black epoxy structural adhesive, reinforced, bicomponent and non-discovery, which provides good overall resistance as well as high impact resistance and fatigue to meet the most demanding union challenges. The epoxy adhesive 3MTM Scotch-Weld DP420NS can replace mechanical braces, screws, rivets and welding points in many applications.

Recommended applications: Unions with reduced contact surfaces, Heavy duty mounts, Metal work, Union with carbon fiber epoxy.

TECHNICAL DATA

The epoxy adhesive 3MTM Scotch-WeldTM DP420 maintains its bond resistance at high and low temperatures and can withstand powder paint operations up to 204 °C for 60 minutes.

The epoxy adhesive 3MTM Scotch-WeldTM DP420 cream color meets the requirements of UL 94 HB.

The mixing ratio is 2:1 and offers a mixing life of 20 minutes, enough to make the necessary settings before it heals. This adhesive is available in presentations of different sizes and can be dispensed in various ways to meet the demands of various users and jobs.

ON THE 3M

3M has such diverse solutions that have the right answer to each need. And if not, they work with the customer to develop that new way of doing things. This different way of thinking is shown in developed studies to find the most optimal product for each organization.